High temperature severe wear compound

FOB Reference Price:Get Latest Price
Report Suspicious Activity
Overview
Quick Details
Classification:
Chemical Auxiliary Agent

Specifications

MXHT
High temperature severe wear compound

An advanced ceramic reinforced composite for protection agaisnt sliding wear and chemical attack at elevated temperatures.  ARC  MXHT is trowel applied at thicknesses from 6-9 mm (.25-.375") or more.
Technical Data
Dry Temperature Dry (Min/Max)
-20 F (-29C) to 466 F (230 C)
Wet Temperature (Min/Max)
-20 F (-29C) to 266 F (130 C)
Compressive Strength - kg/cm2 - Mpa (psi)
1,652 - 162 (23,500)
Flexural Strength - kg/cm2 - Mpa (psi)569 - 55 (8,100)
Tensile Strength - kg/cm2/Mpa (psi)302 - 29 (4,300)
Tensile Adhesion - kg/cm2 - Mpa (psi)
Greater than 140 - 14 (2,000)
Impact Resistance - nt m (in. lbs.)
>13 N-m (>120 in-lb)
Water Vapor Permeability (meteric perm-cm - Perms)
Salt Fog
Shore D Hardness
89